DFM-103 Blend Polyols

DFM-103 Blend Polyols
Product Detailed
Related Categories:Polymer
Related Product Searches:DFM-103 Blend Polyols,High Quality,Polyols,Polyether
It has high mechanical strength and rigidity, simple molding process , high production efficiency, good appearance

DFM-103 Blend Polyols 

Products Introduction

Imitate wood foam, is a new type of carving synthetic materials. It has high mechanical strength and rigidity, simple molding process , high production efficiency, good appearance.

Characteristics are as follows :

1. excellent repetition molding property.  It not only can mould certain shape size, but also mould  lifelike wood texture and other designs, good feel of touch

2. appearance and feel close to wood , which could be planed, nailed, drilled, and carved patterns or designs .

3. mould can only be produced using aluminum or steel, but can use silicon rubber, epoxy resin or other resin, which are low cost and easy machining.

4. molding process is simple, fast, high efficiency of qualified.

5. physical and mechanical properties is one of optimal synthesis wood  produced by various polymer . Physical property can be controled by adjusting the formula.

Physical Property

Appearance              

Hydroxyl value           mgKOH/g Viscosity  25°C   mPa.s

Density  20 °C          g/ml

Storage temperature          

Storage stability             Month

Light yellow to brown yellow viscous liquid

250-400

600-1000

1.10±0.02

10-25

6

Recommended Ratio

pbw

DFM-103 polyols

Isocyanate

100

100-105

 Reactivity Characteristics

Actual value varies as per processing conditions.

Rise time        s

Gel time         s

Tack free time    s

Free density  kg/m3

50-70

140-160

200-220

90-250

Foam Performance

mouldingdensity 

Curving  strength

Compressive strength

Tensile  strength

Surface strength

shrinking percentage 

Kg/m3

MPa

MPa

MPa

Shore D

%

300-600

7-20

10-20

10-25

50-80

≤0.3

DFM-103 Blend Polyols